Experimental and theoretical analysis of the mass transport through porous glass membranes with different pore diameters
Buch in deiner Nähe kaufen
Beschreibung
The understanding of mass transport in narrow pores, it is an important problem of long standing interest in heterogeneous catalysis, gas-solid reactions and adsorptive separations. In recent years intense worldwide activity in applying newly developed porous materials has led to renewed interest in this subject.
This work was focused on studying single gas and competitive diffusion through porous glass membranes with different mean pore sizes in the range from 1.4 to 4.2 nm and through a Vycor glass membrane with mean pore size of 4 nm.
In this thesis a comprehensive experimental data basis of pure component diffusion and counter-diffusion of different test gases was provided. Besides studying diffusion, the adsorption equilibrium measurements were performed to determine pure and binary mixture isotherms.
Das Verständnis der Transportvorgänge in kleinen Poren ist von großer Bedeutung für die Gebiete der heterogenen Katalyse, der Gas-Feststoff-Reaktionen und der adsorptiven Stofftrennung. In den letzten Jahren wurde das Interesse an diesem Thema durch die weltweite Anwendung neuartiger poröser Materialien neu entfacht.
Das Ziel dieser Studie war die Untersuchung der Einzelgas- und Gegendiffusion durch poröse Glasmembranen mit Porendurchmessern zwischen 1,4 und 4,2 nm und durch Vycor-Glas mit einem mittleren Porendurchmesser von 4 nm.
Diese Studie basiert auf umfangreichen experimentellen Daten sowohl der Einzelgas- als auch der Gegendiffusion von Gasgemischen. Zudem wurden Adsorptionsisothermen für reine Gase und binäre Gasmischungen ermittelt.