Study of New Ternary Rare-Earth Intermetallic Germanides with Polar Covalent Bonding
Beyond the Zintl Picture
Buch in deiner Nähe kaufen
Beschreibung
The thesis focuses on the syntheses, structural characterizations and chemical bonding analyses for several ternary R–M–Ge (R = rare earth metal; M = another metal) intermetallics. The challenges in understanding the main interactions governing the chemistry of these compounds, which lead to our inability to predict their formation, structure and properties, are what provided the motivation for this study. In particular, the R2MGe6 (M = Li, Mg, Al, Cu, Zn, Pd, Ag), R4MGe10-x (M = Li, Mg), R2Pd3Ge5, Lu5Pd4Ge8, Lu3Pd4Ge4 and Yb2PdGe3 phases were synthesized and structurally characterized. Much effort was put into the stabilization of metastable phases, employing the innovative metal flux method, and into the accurate structure solution of twinned crystals. Cutting-edge position-space chemical bonding techniques were combined with newmethodologies conceived to correctly describe the Ge–M, Ge–La and also La–M polar-covalent interactions for the La2MGe6 (M = Li, Mg, Al, Cu, Zn, Pd, Ag) series. The present results constitute a step forward in our comprehension of ternary germanide chemistry as well as providing a good playground for further investigations.
The thesis focuses on the syntheses, structural characterizations and chemical bonding analyses for several ternary R–M–Ge (R = rare earth metal; M = another metal) intermetallics. The challenges in understanding the main interactions governing the chemistry of these compounds, which lead to our inability to predict their formation, structure and properties, are what provided the motivation for this study. In particular, the R2MGe6 (M = Li, Mg, Al, Cu, Zn, Pd, Ag), R4MGe10-x (M = Li, Mg), R2Pd3Ge5, Lu5Pd4Ge8, Lu3Pd4Ge4 and Yb2PdGe3 phases were synthesized and structurally characterized. Much effort was put into the stabilization of metastable phases, employing the innovative metal flux method, and into the accurate structure solution of twinned crystals. Cutting-edge position-space chemical bonding techniques were combined with newmethodologies conceived to correctly describe the Ge–M, Ge–La and also La–M polar-covalent interactions for the La2MGe6 (M = Li, Mg, Al, Cu, Zn, Pd, Ag) series. The present results constitute a step forward in our comprehension of ternary germanide chemistry as well as providing a good playground for further investigations.
Nominated as an outstanding Ph.D. thesis by the Max Planck Institute for Chemical Physics of Solids, Dresden, Germany Provides a didactic overview of the main experimental and theoretical methodologies employed nowadays in the field of intermetallic chemistry Presents in detail the synthetic procedures, metallographic characterization and crystal structure determination of several ternary rare-earth germanides Discusses chemical bonding using state of the art position-space techniques proposing also new and sophisticated tools
Autor*in
Riccardo Freccero
Themen in »Study of New Ternary Rare-Earth Intermetallic Germanides with Polar Covalent Bonding«
Intermetallic Compounds Rare-Earth Germanides Zintl Phases Polar Intermetallics Metal Flux Synthesis Symmetry Reduction Chemical Bonding Electron Localizability Indicator Quantum Theory of Atoms in Molecules 8-N Rule